EPU Flooring
Description
Three component, solvent free, flexible, self levelling EPU (epoxy- polyurethane) flooring
Features: -
Self levelling coatings with excellent flow & levelling characteristics
Conforms to the Global Migration Standards laid down in US-FDA: 21CFR 175-300
Very high abrasion, impact and mar resistance
Excellent flexibility and tensile strength
Resistance to aggressive corrosive environment
Excellent inter-coat adhesion over aged/ old epoxy coatings
Technical Properties: -
Recommended DFT / Coat 1 – 2 mm
Theoretical Covering Capacity 0.32 Sq.Mtr /kg @ 2 mm DFT (0.5 Sq.Mtr/ litre) 0.64 Sq.Mtr /kg @ 1 mm DFT (1.0 Sq.Mtr/ litre)
Drying Time Surface Dry: 6 hours
Hard Dry: 24 hours
Full Cure: 7 days
Mixing Ratio (by weight) Base : Hardener : Aggregate (Base to aggregate ratio would vary with shade) 36.5 : 16.5 : 47.0
Pot life :30 minutes
Mechanical Properties: -
Compressive Strength (ASTM C 579) 72 MPa
Flexural Strength (ASTM C 580) 32 MPa
Tensile Strength (ASTM C 307) 18 Mpa
For application and safety instructions download TDS and MSDS.
Click Here to Download TDS
Description
Starothane RCI Gloss is a three-component solvent free EPU coating. It is a high-performance product. It is a self-smoothing, easy to apply product, leaving a seamless surface with glossy finish. It has excellent chemical, abrasion and impact resistance. If enhanced slip resistance is required Staroxy Anti-Skid can be used in the system. To be used as finish coat in atmospheric environments. Can be applied directly on approved primers depending on the conditions of the concrete substrate.
Features:
High flexibility
Provides a hard wearing, chemical & abrasion resistant top coat
Excellent flow and levelling characteristics giving self levelled finish
High gloss
Excellent adhesion over primed surface
Conforms to the Global Migration Standards laid down in US-FDA: 21CFR 175-300
Solvent free; no odour during application
Easy to clean and maintain
Finds application in pharma, food, breweries, automobile, chemical and light engineering industries
Technical Properties:
Generic Type: Hybrid EPU based
Volume Solids: 62% - 66%
Ratio: Pre weighted pack of 23 Kg
Covering Capacity: 1.4 m2 per kg for 0.5 mm thickness
Coverage: 32 Sq. Mtr. For 0.5 mm thickness
Dry Time:
To Touch – 8 Hrs.
To Recoat – 14 Hrs.
Foot Traffic – 14 Hrs.
Full Cure – 7 Days
Pot Life: 30 Minutes
Mechanical Properties:
Volume Solids (ASTM D 2697): 100%
Flexural Strength: 40 N/mm2
Tensile Strength: 20 N/mm2
Bond Strength: Greater than cohesive strength of quality
For Application Instructions and Storage Condition requirements please download TDS.
Click Here to Download TDS
Description
Starothane RCI Gloss is a three-component solvent free EPU coating. It is a high-performance product. It is a self-smoothing, easy to apply product, leaving a seamless surface with matt finish. It has excellent chemical, abrasion and impact resistance. If enhanced slip resistance is required Staroxy Anti-Skid can be used in the system. To be used as finish coat in atmospheric environments. Can be applied directly on approved primers depending on the conditions of the concrete substrate.
Features:
High flexibility
Provides a hard wearing, chemical & abrasion resistant top coat
Excellent flow and levelling characteristics giving self levelled finish
Matt finish.
Excellent adhesion over primed surface
Conforms to the Global Migration Standards laid down in US-FDA: 21CFR 175-300
Solvent free; no odour during application
Easy to clean and maintain
Finds application in pharma, food, breweries, automobile, chemical and light engineering industries
Technical Properties:
Generic Type: Hybrid EPU based
Volume Solids: 62% - 66%
Ratio: Pre weighted pack of 23 Kg
Covering Capacity: 1.4 m2 per kg for 0.5 mm thickness
Coverage: 32 Sq. Mtr. For 0.5 mm thickness
Dry Time:
To Touch – 8 Hrs.
To Recoat – 14 Hrs.
Foot Traffic – 14 Hrs.
Full Cure – 7 Days
Pot Life: 30 Minutes
Mechanical Properties:
Volume Solids (ASTM D 2697): 100%
Flexural Strength: 40 N/mm2
Tensile Strength: 20 N/mm2
Bond Strength: Greater than cohesive strength of quality
For Application Instructions and Storage Condition requirements please download TDS.
Click Here to Download TDS